Preparation of collagen-based materials for wound dressing

摘要Objective To describe the methods which were used to develop collagen-based materials for wound dressing.Methods Fresh frozen bovine tendon was treated with 0.05 mol/L acetic acid at pH 3.2 for 48-72 hours, homogenized, filtered, mixed with 8% chondroitin sulphate, for creating a deaerated 1.5%-2.5% collagen solution. The solution was lyophilized in either a pre-frozen or non-pre-frozen mould. The collagen sponge was then cross-linked with 0.25% glutaraldehyde for 24 hours. Three other types of wound dressings were developed using a similar method: collagen membrane with a polyurethane membrane onlay, polyurethane-coated collagen membrane and collagen membrane on gauze.Results It was demonstrated that the use of frozen bovine tendon was stable, and that the prepared collagen sponge contained pores of 50-400 μm in diameter. Conclusions Collagen could be used as wound dressing.

更多
广告
作者 吴志谷 [1] 盛志勇 [1] 孙同柱 [1] 耿淼 [1] 黎君友 [1] 姚咏明 [1] 黄祖琇 [2] 学术成果认领
作者单位 Burn Institute, 304th Hospital, Beijing 100037, China [1] Department of Chemistry, Beijing University, Beijing 100871, China [2]
分类号 R318
栏目名称
发布时间 2004-01-08
提交
  • 浏览131
  • 下载0
中华医学杂志(英文版)

中华医学杂志(英文版)

2003年116卷3期

419-423页

SCIMEDLINEISTICCSCDCABP

加载中!

相似文献

  • 中文期刊
  • 外文期刊
  • 学位论文
  • 会议论文

加载中!

加载中!

加载中!

加载中!

特别提示:本网站仅提供医学学术资源服务,不销售任何药品和器械,有关药品和器械的销售信息,请查阅其他网站。

  • 客服热线:4000-115-888 转3 (周一至周五:8:00至17:00)

  • |
  • 客服邮箱:yiyao@wanfangdata.com.cn

  • 违法和不良信息举报电话:4000-115-888,举报邮箱:problem@wanfangdata.com.cn,举报专区

官方微信
万方医学小程序
new翻译 充值 订阅 收藏 移动端

官方微信

万方医学小程序

使用
帮助
Alternate Text
调查问卷